是否进口否 | 厂家(产地)注塑 |
牌号DF002ERH | 用途级别注塑 |
是否进口否 | 厂家(产地)注塑 |
牌号DF002ERH | 用途级别注塑 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | 1) | |||
Tensile Stress, break | 83 | MPa | ASTM D638 | |
Tensile Strain, break | 3.8 | % | ASTM D638 | |
Tensile Modulus, 50 mm/min | 4170 | MPa | ASTM D638 | |
Flexural Stress | 149 | MPa | ASTM D790 | |
Flexural Modulus | 4280 | MPa | ASTM D790 | |
Tensile Stress, break | 84 | MPa | ISO 527 | |
Tensile Strain, break | 3.6 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 4100 | MPa | ISO 527 | |
Flexural Stress | 117 | MPa | ISO 178 | |
Flexural Modulus | 3920 | MPa | ISO 178 | |
IMPACT | 1) | |||
Izod Impact, unnotched, 23掳C | 929 | J/m | ASTM D4812 | |
Izod Impact, notched, 23掳C | 97 | J/m | ASTM D256 | |
Instrumented Dart Impact Energy @ peak, 23掳C | 13 | J | ASTM D3763 | |
Multiaxial Impact | 9 | J | ISO 6603 | |
Izod Impact, unnotched 80*10*4 +23掳C | 61 | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 8 | kJ/m虏 | ISO 180/1A | |
THERMAL | 1) | |||
HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | 掳C | ASTM D648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 136 | 掳C | ASTM D648 | |
CTE, -40掳C to 40掳C, flow | 3.81E-05 | 1/掳C | ASTM E831 | |
CTE, -40掳C to 40掳C, xflow | 5.34E-05 | 1/掳C | ASTM E831 | |
CTE, -40掳C to 40掳C, flow | 3.82E-05 | 1/掳C | ISO 11359-2 | |
CTE, -40掳C to 40掳C, xflow | 5.35E-05 | 1/掳C | ISO 11359-2 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | 掳C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 137 | 掳C | ISO 75/Af | |
PHYSICAL | 1) | |||
Density | 1.275 | g/cm鲁 | ASTM D792 | |
Moisture Absorption, (23掳C/50% RH/24 hrs) | 0.15 | % | ASTM D570 | |
Mold Shrinkage, flow, 24 hrs | 3) | 0.4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 3) | 0.5 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 3) | 0.43 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 3) | 0.51 | % | ISO 294 |
Density | 1.27 | g/cm鲁 | ISO 1183 | |
INJECTION MOLDING | 2) | |||
Drying Temperature | 120 | 掳C | ||
Drying Time | 4 | Hrs | ||
Maximum Moisture Content | 0.02 | % | ||
Melt Temperature | 305-325 | 掳C | ||
Front - Zone 3 Temperature | 320-330 | 掳C | ||
Middle - Zone 2 Temperature | 310-320 | 掳C | ||
Rear - Zone 1 Temperature | 295-305 | 掳C | ||
Mold Temperature | 80-110 | 掳C | ||
Back Pressure | 0.2-0.3 | MPa | ||
Screw Speed | 30-60 | rpm |
企业类型 | 有限责任公司(自然人独资) | 统一社会信用代码 | 91441900MA4UNCL112 |
---|---|---|---|
成立日期 | 2016-04-07 | 法定代表人/负责人 | 吴双发 |
注册资本 | 50万(元) | 注册地址 | 东莞市樟木头镇先威大道85-1号塑胶商务中心二期9栋32号 |
营业期限 | 2016-04-07 至 无固定期限 | 登记机关 | 东莞市市场监督管理局 |
经营范围 | 销售:塑胶原料、其他化工产品(不含危险化学品)、高分子材料。(依法须经批准的项目,经相关部门批准后方可开展经营活动)〓 |