| 是否进口否 | 产地美国 |
| 厂家(产地)美国苏威 | 牌号A-4133 L |
| 销售方式品牌经销 | 类型标准料 |
| 加工级别注塑级 | 特性级别增强级、 耐高温、 标准级 |
| 用途级别汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| 是否进口否 | 产地美国 |
| 厂家(产地)美国苏威 | 牌号A-4133 L |
| 销售方式品牌经销 | 类型标准料 |
| 加工级别注塑级 | 特性级别增强级、 耐高温、 标准级 |
| 用途级别汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | *** 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.29 % @Time 86400 sec | 0.29 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.7 MPa @Temperature 175 °C | 11700 psi @Temperature 347 °F | *** 527-2 |
| 89.6 MPa @Temperature 150 °C | 13000 psi @Temperature 302 °F | *** 527-2 | |
| 134 MPa @Temperature 100 °C | 19400 psi @Temperature 212 °F | *** 527-2 | |
| 193 MPa @Temperature 23.0 °C | 28000 psi @Temperature 73.4 °F | *** 527-2 | |
| Tensile Strength | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 1.9 % @Temperature 23.0 °C | 1.9 % @Temperature 73.4 °F | *** 527-2 | |
| 3.3 % @Temperature 100 °C | 3.3 % @Temperature 212 °F | *** 527-2 | |
| 3.3 % @Temperature 150 °C | 3.3 % @Temperature 302 °F | *** 527-2 | |
| 4.0 % @Temperature 175 °C | 4.0 % @Temperature 347 °F | *** 527-2 | |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 |
| 5.79 GPa @Temperature 175 °C | 840 ksi @Temperature 347 °F | *** 527-2 | |
| 6.41 GPa @Temperature 150 °C | 930 ksi @Temperature 302 °F | *** 527-2 | |
| 8.96 GPa @Temperature 100 °C | 1300 ksi @Temperature 212 °F | *** 527-2 | |
| 12.3 GPa @Temperature 23.0 °C | 1780 ksi @Temperature 73.4 °F | *** 527-2 | |
| Flexural Strength | 290 MPa | 42100 psi | ASTM D790 |
| 114 MPa @Temperature 175 °C | 16500 psi @Temperature 347 °F | *** 178 | |
| 128 MPa @Temperature 150 °C | 18600 psi @Temperature 302 °F | *** 178 | |
| 187 MPa @Temperature 100 °C | 27100 psi @Temperature 212 °F | *** 178 | |
| 269 MPa @Temperature 23.0 °C | 39000 psi @Temperature 73.4 °F | *** 178 | |
| Flexural Modulus | 12.3 GPa | 1780 ksi | ASTM D790 |
| 4.90 GPa @Temperature 175 °C | 711 ksi @Temperature 347 °F | *** 178 | |
| 5.17 GPa @Temperature 150 °C | 750 ksi @Temperature 302 °F | *** 178 | |
| 7.72 GPa @Temperature 100 °C | 1120 ksi @Temperature 212 °F | *** 178 | |
| 10.4 GPa @Temperature 23.0 °C | 1510 ksi @Temperature 73.4 °F | *** 178 | |
| Compressive Strength | 162 MPa | 23500 psi | ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Modulus | 4.15 - 4.36 GPa | 602 - 632 ksi | Calculated |
| Shear Strength | 89.6 MPa | 13000 psi | ASTM D732 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (***) | 8.20 kJ/m² | 3.90 ft-lb/in² | *** 180/1A |
| 54.6 kJ/m² | 26.0 ft-lb/in² | *** 180/1U | |
| Charpy Impact Unnotched | 8.60 J/cm² | 40.9 ft-lb/in² | *** 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | *** 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C @Temperature 100 - 200 °C | 6.11 µin/in-°F @Temperature 212 - 392 °F | TMA; ASTM E831 |
| 22.0 µm/m-°C @Temperature 0.000 - 100 °C | 12.2 µin/in-°F @Temperature 32.0 - 212 °F | TMA; ASTM E831 | |
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C @Temperature 0.000 - 100 °C | 42.8 µin/in-°F @Temperature 32.0 - 212 °F | TMA; ASTM E831 |
| 140 µm/m-°C @Temperature 100 - 200 °C | 77.8 µin/in-°F @Temperature 212 - 392 °F | TMA; ASTM E831 | |
| Melting Point | 327 °C | 621 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 320 °C @Thickness 3.20 mm | 608 °F @Thickness 0.126 in | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C | 590 °F | Unannealed; *** 75-2/A |
| 300 °C @Thickness 3.20 mm | 572 °F @Thickness 0.126 in | Annealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | UL 94 |
本公司长期销售 美国苏威 PPA，PPS，PAEK，PAI，PFA，PEEK, PPSU ,PSU ,PES，PARA，PAEK ，PTFE，PVDF ，ECTFE料多种型号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电，竭诚为您服务！
| 企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
|---|---|---|---|
| 成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
| 注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
| 登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售：塑胶原料、化工原料（不含危险化学品）。 |
查看联系方式
东莞市樟木头双浩塑胶原料经营部
余先生