是否进口否 | 产地美国 |
厂家(产地)沙伯基础(原GE) | 牌号1000EF |
销售方式品牌经销 | 类型标准料 |
加工级别注塑级 | 特性级别标准级 |
用途级别汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
是否进口否 | 产地美国 |
厂家(产地)沙伯基础(原GE) | 牌号1000EF |
销售方式品牌经销 | 类型标准料 |
加工级别注塑级 | 特性级别标准级 |
用途级别汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
Density | 1.27 g/cc | 0.0459 lb/in? | ISO 1183 |
Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ASTM D570 |
0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ISO 62-1 | |
Moisture Absorption | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Extrusion Blow Molding |
0.0200 % | 0.0200 % | Injection Molding | |
0.200 % | 0.200 % | 23°C/50% RH/24 hrs; ISO 62-4 | |
Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C/50% RH; ISO 62-4 |
Water Absorption at Saturation | 1.25 % | 1.25 % | ASTM D570 |
1.25 % | 1.25 % | ISO 62-1 | |
Viscosity | 13 cP @Load 5.00 kg, Temperature 360 °C | 13 cP @Load 11.0 lb, Temperature 680 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 9.0 g/10 min @Load 6.60 kg, Temperature 337 °C | 9.0 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 106 | 106 | ISO 2039-2 |
109 | 109 | ASTM D785 | |
Ball Indentation Hardness | 140 MPa | 20300 psi | H358/30; ISO 2039-1 |
Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ASTM D638 |
110 MPa | 16000 psi | 50 mm/min; ISO 527 | |
115 MPa | 16700 psi | 50 mm/min; ASTM D638 | |
Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
60 % | 60 % | 5 mm/min; ASTM D638 | |
60 % | 60 % | 50 mm/min; ASTM D638 | |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
7.0 % | 7.0 % | 5 mm/min; ASTM D638 | |
7.0 % | 7.0 % | 50 mm/min; ASTM D638 | |
Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
3.35 GPa | 486 ksi | 5 mm/min; ASTM D638 | |
Flexural Strength | 160 MPa | 23200 psi | yld, 2.6 mm/min, 100 mm span; ASTM D790 |
160 MPa | 23200 psi | yield, 2 mm/min; ISO 178 | |
165 MPa | 23900 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 3.20 GPa | 464 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
3.30 GPa | 479 ksi | 2 mm/min; ISO 178 | |
3.40 GPa | 493 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
Poissons Ratio | 0.36 | 0.36 | ASTM E132 |
Izod Impact Notched | 53.0 J | 39.1 ft-lb | ASTM D256 |
50.0 J @Temperature -30.0 °C | 36.9 ft-lb @Temperature -22.0 °F | ASTM D256 | |
1335 J @Thickness 3.20 mm | 984.6 ft-lb @Thickness 0.126 in | reverse notched; ASTM D256 | |
Izod Impact, Unnotched | 18.0 J/cm | 33.7 ft-lb/in | ASTM D4812 |
15.4 J/cm @Temperature -30.0 °C | 28.9 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |
Izod Impact, Notched (ISO) | 6.00 kJ/m? | 2.86 ft-lb/in? | 80*10*4; ISO 180/1A |
6.00 kJ/m? @Temperature -30.0 °C | 2.86 ft-lb/in? @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
Charpy Impact, Notched | 0.400 J/cm? | 1.90 ft-lb/in? | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
0.400 J/cm? @Temperature -30.0 °C | 1.90 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
Gardner Impact | 36.0 J | 26.6 ft-lb | ASTM D3029 |
Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 52.0 ?m/m-°C @Temperature -20.0 - 150 °C | 28.9 ?in/in-°F @Temperature -4.00 - 302 °F | ISO 11359-2 |
56.0 ?m/m-°C @Temperature -20.0 - 150 °C | 31.1 ?in/in-°F @Temperature -4.00 - 302 °F | ASTM E831 | |
CTE, linear, Transverse to Flow | 52.0 ?m/m-°C @Temperature -20.0 - 150 °C | 28.9 ?in/in-°F @Temperature -4.00 - 302 °F | ISO 11359-2 |
54.0 ?m/m-°C @Temperature -20.0 - 150 °C | 30.0 ?in/in-°F @Temperature -4.00 - 302 °F | ASTM E831 | |
Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft?-°F | ASTM C177 |
0.220 W/m-K | 1.53 BTU-in/hr-ft?-°F | ISO 8302 | |
Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
210 °C @Thickness 6.40 mm | 410 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
190 °C @Thickness 3.20 mm | 374 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
201 °C @Thickness 6.40 mm | 394 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ASTM D1525 |
211 °C | 412 °F | Rate B/50; ISO 306 | |
212 °C | 414 °F | Rate B/120; ISO 306 | |
215 °C | 419 °F | Rate A/50; ISO 306 | |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 345 - 405 °C | 653 - 761 °F | |
Zone 1 | 325 - 350 °C | 617 - 662 °F | Extrusion Blow Molding |
Zone 2 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
340 - 405 °C | 644 - 761 °F | ||
Zone 3 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
345 - 415 °C | 653 - 779 °F | ||
Zone 4 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
Zone 5 | 330 - 355 °C | 626 - 671 °F | |
Die Temperature | 325 - 355 °C | 617 - 671 °F | Extrusion Blow Molding |
Melt Temperature | 320 - 355 °C | 608 - 671 °F | Extrusion Blow Molding |
350 - 410 °C | 662 - 770 °F | Injection Molding | |
Head Temperature | 330 - 355 °C | 626 - 671 °F | Zone 6 - Top Temperature |
330 - 355 °C | 626 - 671 °F | Zone 7 - Bottom Temperature | |
Mold Temperature | 65.0 - 175 °C | 149 - 347 °F | |
135 - 180 °C | 275 - 356 °F | ||
Drying Temperature | 140 - 150 °C | 284 - 302 °F | Extrusion Blow Molding |
150 °C | 302 °F | Injection Molding | |
Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
4.00 - 6.00 hour | 4.00 - 6.00 hour | Extrusion Blow Molding | |
24.0 hour | 24.0 hour | Cumulative; Injection Molding | |
24.0 hour | 24.0 hour | Cumulative; Extrusion Blow Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 10 - 70 rpm | 10 - 70 rpm | |
Descriptive Properties | |||
Screw speed (Circumferential speed) | 0.2-0.3 m/s |
本公司长期销售沙伯基础 PEI,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PC料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!
企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
---|---|---|---|
成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售:塑胶原料、化工原料(不含危险化学品)。 |