| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | *** 1183 |
| Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
| 0.150 % | 0.150 % | 23°C / 50% RH; *** 62 | |
| Water Absorption at Saturation | 0.35 % | 0.35 % | *** 62-1 |
| Viscosity | 9.0 cP @Load 1.20 kg, Temperature 300 °C | 9.0 cP @Load 2.65 lb, Temperature 572 °F | MVR cc/10 min; *** 1133 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C | 10 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; *** 527 |
| 73.0 MPa | 10600 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 50 mm/min; *** 527 | |
| Elongation at Break | >= 100 % | >= 100 % | 50 mm/min; ASTM D638 |
| >= 100 % | >= 100 % | 50 mm/min; *** 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; *** 527 |
| 6.4 % | 6.4 % | 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; *** 527 |
| 2.40 GPa | 348 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 100 MPa | 14500 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 |
| 100 MPa | 14500 psi | yield, 2 mm/min; *** 178 | |
| Flexural Modulus | 2.45 GPa | 355 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.45 GPa | 355 ksi | 2 mm/min; *** 178 | |
| Izod Impact Notched | 820 J | 605 ft-lb | ASTM D256 |
| 130 J @Temperature -30.0 °C | 95.9 ft-lb @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (***) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*3; *** 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 80*10*3; *** 180/1A | |
| Izod Impact, Unnotched (***) | NB | NB | 80*10*3; *** 180/1U |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; *** 179/1eU |
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | Edgew 80*10*3 sp=62mm; *** 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; *** 179/1eA | |
| Dart Drop, Total Energy | 85.0 J | 62.7 ft-lb | ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec @Thickness >=1.00 mm | 30 - 60 sec @Thickness >=0.0394 in | UL 746A |
| >= 120 sec @Thickness >=3.00 mm | >= 120 sec @Thickness >=0.118 in | UL 746A | |
| High Amp Arc Ignition, HAI | 60 - 120 arcs @Thickness >=1.00 mm | 60 - 120 arcs @Thickness >=0.0394 in | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | *** 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | *** 11359-2 | |
| Hot Ball Pressure Test | 75.0 °C | 167 °F | PASS; IEC 60695-10-2 |
| 125 °C | 257 °F | PASS; IEC 60695-10-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; *** 75/Af |
| 126 °C @Thickness 3.20 mm | 259 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 140 °C | 284 °F | Rate B/50; *** 306 |
| 140 °C | 284 °F | Rate B/50; ASTM D1525 | |
| 141 °C | 286 °F | Rate B/120; *** 306 | |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness >=1.50 mm | V-2 @Thickness >=0.0591 in | UL 94 |
| Glow Wire Ignition Temperature | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-13 |
| 850 °C @Thickness 1.50 mm | 1560 °F @Thickness 0.0591 in | IEC 60695-2-13 | |
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | IEC 60695-2-13 | |
| Glow Wire Flammability Index | 900 °C @Thickness 1.50 mm | 1650 °F @Thickness 0.0591 in | IEC 60695-2-12 |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |
| 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 60695-2-12 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.59 | 1.59 | *** 489 |
| Haze | 0.20 % @Thickness 2.54 mm | 0.20 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 89 % @Thickness 2.54 mm | 89 % @Thickness 0.100 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 275 - 295 °C | 527 - 563 °F | |
| Zone 2 | 265 - 290 °C | 509 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | |
| Descriptive Properties | |||
| UV-light, water exposure/immersion | F1 | UL 746C |
本公司长期销售沙伯基础 PC，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！
| 企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
|---|---|---|---|
| 成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
| 注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
| 登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售：塑胶原料、化工原料（不含危险化学品）。 |
查看联系方式
东莞市樟木头双浩塑胶原料经营部
余先生