| 牌号B30S | 产商/产地德国/无锡 |
| 含量≥99％ | 品牌朗盛 |
| 纯度99% | 密度1.14kg/m3 |
| 用途标准注塑级 | CAS32131-17-2 |
供应德国朗盛B30S标准注塑级尼龙6塑胶原料，标准注射级，易流动，成型周期短，易脱摸，快速固化，宜制通用制品。
德国朗盛Durethan B30S物性物性：
| Physical | Dry | Conditioned | Unit | Test Method |
Specific Gravity | 1.14 | -- | g/cm? | ASTM D792 |
Density | 1.14 | -- | g/cm? | ISO 1183 |
Apparent Density | 0.70 | -- | g/cm? | ISO 60 |
Molding Shrinkage | ISO 2577 | |||
Across Flow: 260°C, 3.00 mm 2 | 1.2 | -- | % | |
Across Flow: 120°C, 4 hr, 3.00 mm 3 | 0.40 | -- | % | |
Flow: 260°C, 3.00 mm 2 | 1.0 | -- | % | |
Flow: 120°C, 4 hr, 3.00 mm 3 | 0.32 | -- | % | |
Water Absorption (Saturation, 23°C) | 10 | -- | % | ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus 4 (23°C) | 3200 | 1100 | MPa | ASTM D638 |
Tensile Modulus (23°C) | 3200 | 1000 | MPa | ISO 527-2/1 |
Tensile Strength (Yield, 23°C) | 80.0 | 40.0 | MPa | ASTM D638 |
Tensile Stress (Yield, 23°C) | 80.0 | 40.0 | MPa | ISO 527-2/50 |
Tensile Strength (Break, 23°C) | 50.0 | 60.0 | MPa | ASTM D638 |
Tensile Elongation (Yield, 23°C) | 4.0 | 20 | % | ASTM D638 |
Tensile Strain (Yield, 23°C) | 4.0 | 20 | % | ISO 527-2/50 |
Tensile Elongation (Break, 23°C) | 35 | > 50 | % | ASTM D1708 |
Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2/50 |
Tensile Creep Modulus (1 hr) | -- | 800 | MPa | ISO 899-1 |
Tensile Creep Modulus (1000 hr) | -- | 600 | MPa | ISO 899-1 |
Flexural Modulus (23°C) | 2700 | 703 | MPa | ASTM D790 |
Flexural Modulus 5 (23°C) | 2900 | 850 | MPa | ISO 178 |
Flexural Strength (5.0% Strain, 23°C) | 115 | 35.0 | MPa | ASTM D790 |
Flexural Strength 5 | ISO 178 | |||
3.5% Strain, 23°C | 95.0 | 25.0 | MPa | |
23°C | 110 | 35.0 | MPa | |
Flexural Strain at Flexural Strength 6 (23°C) | 6.0 | 8.0 | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | <10 | <10 | kJ/m? | |
23°C | <10 | 20 | kJ/m? | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break | ||
Notched Izod Impact (23°C, 3.18 mm) | 59 | 750 | J/m | ASTM D256 |
Notched Izod Impact Strength (23°C) | <10 | <10 | kJ/m? | ISO 180/1A |
Unnotched Izod Impact Strength | ISO 180/1U | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break | ||
Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
-30°C | 10.0 | -- | J | |
23°C | 12.0 | -- | J | |
Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
-30°C | 6540 | -- | N | |
23°C | 5140 | -- | N | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 140 | 50.0 | MPa | ISO 2039-1 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.99 mm) | 180 | -- | °C | ASTM D648 |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | -- | °C | ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.99 mm) | 60.0 | -- | °C | ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/A |
Heat Deflection Temperature (8.0 MPa, Unannealed) | 45.0 | -- | °C | ISO 75-2/C |
Vicat Softening Temperature | ||||
-- | 200 | -- | °C | ISO 306/B50 |
-- | 200 | -- | °C | ISO 306/B120 |
Melting Temperature | 222 | -- | °C | ISO 11357-3 |
CLTE - Flow (23 to 55°C) | 0.00010 | -- | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse (23 to 55°C) | 0.00011 | -- | cm/cm/°C | ISO 11359-2 |
RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
RTI Str (1.50 mm) | 75.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | 1.0E+14 | 1.0E+13 | ohm | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+12 | ohm·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | |||
23°C, 1.00 mm | 30 | 30 | kV/mm | |
23°C, 3.00 mm | 30 | 35 | kV/mm | |
Dielectric Constant 7 | IEC 60250 | |||
50 Hz | 3.80 | 20.0 | ||
23°C, 1 MHz | 3.40 | 4.60 | ||
Relative Permittivity | IEC 60250 | |||
23°C, 100 Hz | 4.00 | 15.0 | ||
23°C, 1 MHz | 3.50 | 4.00 | ||
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz | 0.017 | 0.20 | ||
23°C, 1 MHz | 0.020 | 0.12 | ||
Comparative Tracking Index | -- | 600 | V | ASTM D3638 |
Comparative Tracking Index | IEC 60112 | |||
Solution A | 600 | -- | V | |
Solution B | 600 | -- | V | |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
1.50 mm | V-2 | -- | ||
1.60 mm | V-2 | -- | ||
3.00 mm | V-2 | -- | ||
3.20 mm | V-2 | -- |
订购说明
★公司秉承“以诚为本，信誉至上”的经营宗旨，【诚信***】【服务***】【品质***】创立了自己的经营理念，在客户群树立了良好的***。为您提供充足的货源和专业的技术支持！公司所售之新料均***原厂原包，货真价实!
★公司货源充足，品种齐全，价格合理,量大从优,原厂原包,当天订货当天发货。我公司可以提供原料出厂报告(COA)，认证报告;UL认证、FDA认证、材质证明、ISO，ASTM物性资料、ROHS(SGS)报告、物质安全资料表(MSDS)物性、报价、UL报告、RoSH标准、SGS检测报告等）......
★支持物流，快递和货运; 支持现金，银行转账（广东省内可快递代收）.
★原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
★货物送达后，请***时间检查，发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并在24小时内与东莞佳唯斯塑胶原料有限公司颜小姐联系。
★如发货后未能及时收到，请及时与东莞佳唯斯塑胶原料有限公司颜小姐联系15382847379
★订购说明：自接到订单24小时内发货，广州市 深圳市 珠海市 汕头市 韶关市 河源市 梅州市 惠州市 汕尾市 东莞市 中山市 江门市 佛山市 阳江市 湛江市 茂名市 肇庆市 清远市 潮州市 揭阳市 云浮市等地区送货上门，广东省以外等地区协商物流配送，一次购买数量1000kg以上价格从优，欢迎各界朋友前来订购。
★我们的宗旨：【以优惠的价格给广大客户提供优质的品质。本公司货源充足，品种齐全，价格合理】
| 企业类型 | 有限责任公司 | 注册资本 | 100.00万人民币 |
|---|---|---|---|
| 公司注册地址 | 东莞市樟木头 | 登记机关 | 东莞市工商局 |
| 法定代表人/负责人 | 李海涛 | 公司成立日期 | 2006-04-28 |
| 营业期限 | 长期 | 经营范围 | 工程塑料：PC/ABS、POM、PMMA、PA6、PA66、PC、PBT、PET、PPO、PPS、LCP、K胶、EVA、PA6T、PA9T、PA46、PA12、PA612等 |